QIDI PA12-CF 3D Printer Filament
It greatly improves the mechanical properties and heat resistance of the material, and releases the internal stress during the printing process through the fiber mesh structure, resulting in good dimensional stability of the printed part and no warpage.
Temperature and Humidity Resistance
QIDI TECH PAHT-CF(PPA-CF) Filament's have good tensile and flexural strength performance in both wet and dry environments.
Display of PA12-CF Prints
QIDI PA12-CF has a low coefficient of friction, self-lubricating properties and excellent wear resistance, which can easily meet all kinds of high-strength gears or industrial applications with high wear requirements.
Accessory Compatibility
| Recommended | Not Recommended | |
| Build Plate | QIDI PEI Plate, HF Plate and Smooth Plate | PC Plate |
| Hotend | Hardened Steel Nozzle ( 0.4 / 0.6 / 0.8 mm) Bimetal Nozzle ( 0.4 / 0.6 / 0.8 mm) |
Brass/Copper plated Nozzle (0.2/0.4/0.6/0.8 mm) |
| Glue | PVP glue/ 3D LAC adhesive spray | / |
| Recommended Printing Settings | |
| Drying Settings (Blast Drying Oven) | 80-100 °C，4-6 h |
| Printing and Keeping Container's Humidity | < 15% RH (Sealed, with Desiccant) |
| Nozzle Temperature | 280 - 300 °C |
| Bed Temperature (with Glue) | 40-70 °C |
| Printing Speed | < 30-120 mm/s |
| Physical Properties | |
| Density | 1.09 g/cm³ |
| Water absorption | 2.46 % |
| Heat Deflection Temperature | 78.4 °C |
| Melting Temperature | 167 °C |
| Melt Index | 5.1 g/10 min |
| Mechanical Properties | |
| Tensile Strength | 76.95±1.17 MPa |
| Breaking Elongation Rate | 1.63±0.10 % |
| Bending Modulus | 3915.93±195.30 MPa |
| Bending Strength | 114.12±1.93 MPa |
| Impact Strength | 10.01±0.83 KJ/m2 |
Printing Tips
• PA12-CF material is very sensitive to moisture. Printing after absorbing moisture will result in ozzing, extruding with bubbles and rough surface appearance, thus reducing print quality. It is recommended that put the filament into a dry box (humidity below 15%) immediately after opening the QIDI PAHT-CF vacuum foil bag for printing. Please put the unused filament back into the original aluminum foil bag for sealed storage.
• After the printing, the printed part can be annealed to further improve the strength of QIDI PAHT-CF print part. Annealing conditions: place the printed part at 80-100°C for 4-6 hours and cool to room temperature naturally.
For more details please refer to: Filament Guide on WIKI.
Vacuum Aluminum Foil Packaging
According to the test, the water vapor transmission rate of ordinary sealed packaging is 4.76%, while the water vapor transmission rate of vacuum aluminum foil packaging we use is only 0.014%. It can be seen that vacuum aluminum foil packaging is more water-resistant.
Product Size
QIDI TECH PA12-CF filament 1.75mmWorks perfectly with most FDM 3Dprinters on the market.